Vacuum Casting Material
PC-like PU
PC-like PU is used to manufacture products with mechanical characteristics similar to those of PC materials through vacuum casting processes.
PC-like PU is used to manufacture products with mechanical characteristics similar to those of PC materials through vacuum casting processes.
PC-like PU is used to manufacture products with mechanical characteristics similar to those of PC materials through vacuum casting processes.
| Density | 1.2 (g/㎤) |
| Hardness | 80 (shoreD) |
| Tensile strength | 73 (MPa) |
| Tensile strength | 65 (MPa) |
| Flexural strength | 117 (MPa) |
| Flexural modulus | 2600 (MPa) |
| Elongation at break | 13 (%) |
| Impact strength | >100 (KJ/㎡) |
| Glass transition temperature | 90 (℃) |
| HDT | 80 (℃) |
| Density | 1.2 (g/㎤) |
| Hardness | 80 (shoreD) |
| Tensile strength | 73 (MPa) |
| Tensile strength | 65 (MPa) |
| Flexural strength | 117 (MPa) |
| Flexural modulus | 2600 (MPa) |
| Elongation at break | 13 (%) |
| Impact strength | >100 (KJ/㎡) |
| Glass transition temperature | 90 (℃) |
| HDT | 80 (℃) |
PC-like PU is used to manufacture products with mechanical characteristics similar to those of PC materials through vacuum casting processes.
PC-like PU is used to manufacture products with mechanical characteristics similar to those of PC materials through vacuum casting processes.
| Density | 1.2 (g/㎤) |
| Hardness | 80 (shoreD) |
| Tensile strength | 73 (MPa) |
| Tensile strength | 65 (MPa) |
| Flexural strength | 117 (MPa) |
| Flexural modulus | 2600 (MPa) |
| Elongation at break | 13 (%) |
| Impact strength | >100 (KJ/㎡) |
| Glass transition temperature | 90 (℃) |
| HDT | 80 (℃) |
| Density | 1.2 (g/㎤) |
| Hardness | 80 (shoreD) |
| Tensile strength | 73 (MPa) |
| Tensile strength | 65 (MPa) |
| Flexural strength | 117 (MPa) |
| Flexural modulus | 2600 (MPa) |
| Elongation at break | 13 (%) |
| Impact strength | >100 (KJ/㎡) |
| Glass transition temperature | 90 (℃) |
| HDT | 80 (℃) |