Vacuum Casting Material
ABS-like PU
ABS-like PU is used to manufacture products with mechanical characteristics similar to those of ABS materials through vacuum casting processes.
ABS-like PU is used to manufacture products with mechanical characteristics similar to those of ABS materials through vacuum casting processes.
ABS-like PU is used to manufacture products with mechanical characteristics similar to those of ABS materials through vacuum casting processes.
| Density | 1.2 (g/㎤) |
| Hardness | 81~82 (shoreD) |
| Tensile strength | 84~86 (MPa) |
| Tensile strength | 58 (MPa) |
| Flexural strength | 90~110 (MPa) |
| Flexural modulus | 2100 (MPa) |
| Elongation at break | 13~17 (%) |
| Impact strength | 100~110 (J/M) |
| HDT | 70~100 (℃) |
| Density | 1.2 (g/㎤) |
| Hardness | 81~82 (shoreD) |
| Tensile strength | 84~86 (MPa) |
| Tensile strength | 58 (MPa) |
| Flexural strength | 90~110 (MPa) |
| Flexural modulus | 2100 (MPa) |
| Elongation at break | 13~17 (%) |
| Impact strength | 100~110 (J/M) |
| HDT | 70~100 (℃) |
ABS-like PU is used to manufacture products with mechanical characteristics similar to those of ABS materials through vacuum casting processes.
ABS-like PU is used to manufacture products with mechanical characteristics similar to those of ABS materials through vacuum casting processes.
| Density | 1.2 (g/㎤) |
| Hardness | 81~82 (shoreD) |
| Tensile strength | 84~86 (MPa) |
| Tensile strength | 58 (MPa) |
| Flexural strength | 90~110 (MPa) |
| Flexural modulus | 2100 (MPa) |
| Elongation at break | 13~17 (%) |
| Impact strength | 100~110 (J/M) |
| HDT | 70~100 (℃) |
| Density | 1.2 (g/㎤) |
| Hardness | 81~82 (shoreD) |
| Tensile strength | 84~86 (MPa) |
| Tensile strength | 58 (MPa) |
| Flexural strength | 90~110 (MPa) |
| Flexural modulus | 2100 (MPa) |
| Elongation at break | 13~17 (%) |
| Impact strength | 100~110 (J/M) |
| HDT | 70~100 (℃) |