As the most commonly used material, this is white and has properties similar to ABS plastic. It is suitable for prototypes, custom products, high-precision products, and assembly tests. UV exposure may cause discoloration.
As the most commonly used material, this is white and has properties similar to ABS plastic. It is suitable for prototypes, custom products, high-precision products, and assembly tests. UV exposure may cause discoloration.
| Density | 1.2 (g/㎤) |
| Hardness | 81 (shoreD) |
| Tensile strength | 50 (MPa) |
| Elongation at Break | 12~20 (%) |
| Flexural modulus | 2700 (MPa) |
| Water Absorption | 0.27 (%) |
| HDT(0.45MPa) | 60 (℃) |
| Density | 1.2 (g/㎤) |
| Hardness | 81 (shoreD) |
| Tensile strength | 50 (MPa) |
| Elongation at Break | 12~20 (%) |
| Flexural modulus | 2700 (MPa) |
| Water Absorption | 0.27 (%) |
| HDT(0.45MPa) | 60 (℃) |
As the most commonly used material, this is white and has properties similar to ABS plastic. It is suitable for prototypes, custom products, high-precision products, and assembly tests. UV exposure may cause discoloration.
As the most commonly used material, this is white and has properties similar to ABS plastic. It is suitable for prototypes, custom products, high-precision products, and assembly tests. UV exposure may cause discoloration.
| Density | 1.2 (g/㎤) |
| Hardness | 81 (shoreD) |
| Tensile strength | 50 (MPa) |
| Elongation at Break | 12~20 (%) |
| Flexural modulus | 2700 (MPa) |
| Water Absorption | 0.27 (%) |
| HDT(0.45MPa) | 60 (℃) |
| Density | 1.2 (g/㎤) |
| Hardness | 81 (shoreD) |
| Tensile strength | 50 (MPa) |
| Elongation at Break | 12~20 (%) |
| Flexural modulus | 2700 (MPa) |
| Water Absorption | 0.27 (%) |
| HDT(0.45MPa) | 60 (℃) |