As the most commonly used material, this is black and has properties similar to ABS plastic. It is suitable for prototypes, custom products, high-precision products, and assembly tests. check mark button
As the most commonly used material, this is black and has properties similar to ABS plastic. It is suitable for prototypes, custom products, high-precision products, and assembly tests. check mark button
| Density | 1.2 (g/㎤) |
| Hardness | 80~87 (shoreD) |
| Tensile strength | 41~58 (MPa) |
| Tensile Modulus | 2731 (MPa) |
| Flexural strength | 69~76 (MPa) |
| Flexural modulus | 2792 (MPa) |
| Elongation at break | 11 (%) |
| Water Absorption | 0.75 (%) |
| HDT(0.45MPa) | 60 (℃) |
| Density | 1.2 (g/㎤) |
| Hardness | 80~87 (shoreD) |
| Tensile strength | 41~58 (MPa) |
| Tensile Modulus | 2731 (MPa) |
| Flexural strength | 69~76 (MPa) |
| Flexural modulus | 2792 (MPa) |
| Elongation at break | 11 (%) |
| Water Absorption | 0.75 (%) |
| HDT(0.45MPa) | 60 (℃) |
As the most commonly used material, this is black and has properties similar to ABS plastic. It is suitable for prototypes, custom products, high-precision products, and assembly tests. check mark button
As the most commonly used material, this is black and has properties similar to ABS plastic. It is suitable for prototypes, custom products, high-precision products, and assembly tests. check mark button
| Density | 1.2 (g/㎤) |
| Hardness | 80~87 (shoreD) |
| Tensile strength | 41~58 (MPa) |
| Tensile Modulus | 2731 (MPa) |
| Flexural strength | 69~76 (MPa) |
| Flexural modulus | 2792 (MPa) |
| Elongation at break | 11 (%) |
| Water Absorption | 0.75 (%) |
| HDT(0.45MPa) | 60 (℃) |
| Density | 1.2 (g/㎤) |
| Hardness | 80~87 (shoreD) |
| Tensile strength | 41~58 (MPa) |
| Tensile Modulus | 2731 (MPa) |
| Flexural strength | 69~76 (MPa) |
| Flexural modulus | 2792 (MPa) |
| Elongation at break | 11 (%) |
| Water Absorption | 0.75 (%) |
| HDT(0.45MPa) | 60 (℃) |