A plastic material with a transparent color similar to acrylic and which can be produced as translucent and transparent through surface treatment; suitable for prototypes and custom manufacturing. UV exposure may cause discoloration.
A plastic material with a transparent color similar to acrylic and which can be produced as translucent and transparent through surface treatment; suitable for prototypes and custom manufacturing. UV exposure may cause discoloration.
| Density | 1.2 (g/㎤) |
| Hardness | 72~78 (shoreD) |
| Tensile strength | 25~30 (MPa) |
| Tensile Strength at Break | 56 (MPa) |
| Tensile Modulus | 2880 (MPa) |
| Flexural strength | 85 (MPa) |
| Flexural modulus | 2490 (MPa) |
| Elongation at break | 7.50 (%) |
| Water Absorption | 1.10 (%) |
| Glass transition temperature | 44 (℃) |
| HDT(0.45MPa) | 60 (℃) |
| Density | 1.2 (g/㎤) |
| Hardness | 72~78 (shoreD) |
| Tensile strength | 25~30 (MPa) |
| Tensile Strength at Break | 56 (MPa) |
| Tensile Modulus | 2880 (MPa) |
| Flexural strength | 85 (MPa) |
| Flexural modulus | 2490 (MPa) |
| Elongation at break | 7.50 (%) |
| Water Absorption | 1.10 (%) |
| Glass transition temperature | 44 (℃) |
| HDT(0.45MPa) | 60 (℃) |
A plastic material with a transparent color similar to acrylic and which can be produced as translucent and transparent through surface treatment; suitable for prototypes and custom manufacturing. UV exposure may cause discoloration.
A plastic material with a transparent color similar to acrylic and which can be produced as translucent and transparent through surface treatment; suitable for prototypes and custom manufacturing. UV exposure may cause discoloration.
| Density | 1.2 (g/㎤) |
| Hardness | 72~78 (shoreD) |
| Tensile strength | 25~30 (MPa) |
| Tensile Strength at Break | 56 (MPa) |
| Tensile Modulus | 2880 (MPa) |
| Flexural strength | 85 (MPa) |
| Flexural modulus | 2490 (MPa) |
| Elongation at break | 7.50 (%) |
| Water Absorption | 1.10 (%) |
| Glass transition temperature | 44 (℃) |
| HDT(0.45MPa) | 60 (℃) |
| Density | 1.2 (g/㎤) |
| Hardness | 72~78 (shoreD) |
| Tensile strength | 25~30 (MPa) |
| Tensile Strength at Break | 56 (MPa) |
| Tensile Modulus | 2880 (MPa) |
| Flexural strength | 85 (MPa) |
| Flexural modulus | 2490 (MPa) |
| Elongation at break | 7.50 (%) |
| Water Absorption | 1.10 (%) |
| Glass transition temperature | 44 (℃) |
| HDT(0.45MPa) | 60 (℃) |