MJF Nylon(PA12)
A plastic material capable of producing products with high density and strength; ideal for products requiring strong durability, abrasion and chemical resistance
A plastic material capable of producing products with high density and strength; ideal for products requiring strong durability, abrasion and chemical resistance
A plastic material capable of producing products with high density and strength; ideal for products requiring strong durability, abrasion and chemical resistance
| Density | 1.01 (g/㎤) |
| Tensile strength | 48 (MPa) |
| Elongation at break | 15~20 (%) |
| HDT(1.8MPa) | 95 (℃) |
| HDT(0.45MPa) | 175 (℃) |
| Tensile Modulus | 1700 (MPa) |
| Density | 1.01 (g/㎤) |
| Tensile strength | 48 (MPa) |
| Elongation at break | 15~20 (%) |
| HDT(1.8MPa) | 95 (℃) |
| HDT(0.45MPa) | 175 (℃) |
| Tensile Modulus | 1700 (MPa) |
A plastic material capable of producing products with high density and strength; ideal for products requiring strong durability, abrasion and chemical resistance
A plastic material capable of producing products with high density and strength; ideal for products requiring strong durability, abrasion and chemical resistance
| Density | 1.01 (g/㎤) |
| Tensile strength | 48 (MPa) |
| Elongation at break | 15~20 (%) |
| HDT(1.8MPa) | 95 (℃) |
| HDT(0.45MPa) | 175 (℃) |
| Tensile Modulus | 1700 (MPa) |
| Density | 1.01 (g/㎤) |
| Tensile strength | 48 (MPa) |
| Elongation at break | 15~20 (%) |
| HDT(1.8MPa) | 95 (℃) |
| HDT(0.45MPa) | 175 (℃) |
| Tensile Modulus | 1700 (MPa) |