Photopolymer Resin (3D Printing Only)
ABS-like Heat-resistant Resin
| Density | 1.2 (g/㎤) |
| Hardness | 87 (shoreD) |
| Tensile strength | 65 (kg/㎠) |
| Flexural strength | 110 (MPa) |
| Flexural modulus | 2720 (MPa) |
| Elongation at break | 3~5 (%) |
| Impact strength | 20 (J/m) |
| Glass transition temperature | 135 (℃) |
| HDT | 120 (℃) |
| Thermal Expansion Coefficient | 50~150 (μ m/m℃) |
| Density | 1.2 (g/㎤) |
| Hardness | 87 (shoreD) |
| Tensile strength | 65 (kg/㎠) |
| Flexural strength | 110 (MPa) |
| Flexural modulus | 2720 (MPa) |
| Elongation at break | 3~5 (%) |
| Impact strength | 20 (J/m) |
| Glass transition temperature | 135 (℃) |
| HDT | 120 (℃) |
| Thermal Expansion Coefficient | 50~150 (μ m/m℃) |
| Density | 1.2 (g/㎤) |
| Hardness | 87 (shoreD) |
| Tensile strength | 65 (kg/㎠) |
| Flexural strength | 110 (MPa) |
| Flexural modulus | 2720 (MPa) |
| Elongation at break | 3~5 (%) |
| Impact strength | 20 (J/m) |
| Glass transition temperature | 135 (℃) |
| HDT | 120 (℃) |
| Thermal Expansion Coefficient | 50~150 (μ m/m℃) |
| Density | 1.2 (g/㎤) |
| Hardness | 87 (shoreD) |
| Tensile strength | 65 (kg/㎠) |
| Flexural strength | 110 (MPa) |
| Flexural modulus | 2720 (MPa) |
| Elongation at break | 3~5 (%) |
| Impact strength | 20 (J/m) |
| Glass transition temperature | 135 (℃) |
| HDT | 120 (℃) |
| Thermal Expansion Coefficient | 50~150 (μ m/m℃) |