This is brown and has properties similar to ABS plastic. It is suitable for prototypes, custom products, high-precision products, assembly tests, and figure production. Due to the nature of the material color, surface texture is visible even without painting.
This is brown and has properties similar to ABS plastic. It is suitable for prototypes, custom products, high-precision products, assembly tests, and figure production. Due to the nature of the material color, surface texture is visible even without painting.
| Density | 1.2 (g/㎤) |
| Hardness | 74~80 (shoreD) |
| Tensile strength | 25~30 (MPa) |
| Tensile Modulus | 2150~2370 (MPa) |
| Flexural modulus | 2650~2750 (MPa) |
| Elongation at break | 12~20 (%) |
| Impact strength | 58~68 (J/m) |
| Glass transition temperature | 55~70 (℃) |
| HDT(0.45MPa) | 60 (℃) |
| Density | 1.2 (g/㎤) |
| Hardness | 74~80 (shoreD) |
| Tensile strength | 25~30 (MPa) |
| Tensile Modulus | 2150~2370 (MPa) |
| Flexural modulus | 2650~2750 (MPa) |
| Elongation at break | 12~20 (%) |
| Impact strength | 58~68 (J/m) |
| Glass transition temperature | 55~70 (℃) |
| HDT(0.45MPa) | 60 (℃) |
This is brown and has properties similar to ABS plastic. It is suitable for prototypes, custom products, high-precision products, assembly tests, and figure production. Due to the nature of the material color, surface texture is visible even without painting.
This is brown and has properties similar to ABS plastic. It is suitable for prototypes, custom products, high-precision products, assembly tests, and figure production. Due to the nature of the material color, surface texture is visible even without painting.
| Density | 1.2 (g/㎤) |
| Hardness | 74~80 (shoreD) |
| Tensile strength | 25~30 (MPa) |
| Tensile Modulus | 2150~2370 (MPa) |
| Flexural modulus | 2650~2750 (MPa) |
| Elongation at break | 12~20 (%) |
| Impact strength | 58~68 (J/m) |
| Glass transition temperature | 55~70 (℃) |
| HDT(0.45MPa) | 60 (℃) |
| Density | 1.2 (g/㎤) |
| Hardness | 74~80 (shoreD) |
| Tensile strength | 25~30 (MPa) |
| Tensile Modulus | 2150~2370 (MPa) |
| Flexural modulus | 2650~2750 (MPa) |
| Elongation at break | 12~20 (%) |
| Impact strength | 58~68 (J/m) |
| Glass transition temperature | 55~70 (℃) |
| HDT(0.45MPa) | 60 (℃) |