PA66 has higher thermal stability, tensile strength, and rigidity compared to PA6. However, due to its relatively high moisture absorption rate, exposure to moisture can affect its mechanical properties.
PA66 has higher thermal stability, tensile strength, and rigidity compared to PA6. However, due to its relatively high moisture absorption rate, exposure to moisture can affect its mechanical properties.
| Density | 1.2 (g/㎤) |
| Tensile Modulus | 2.8 – 3.3 (GPa) |
| Tensile Strength | 75 – 85 (MPa) |
| Flexural Modulus | 2.8 – 3.5 (GPa) |
| Elongation | 30 – 60 (%) |
| Hardness | 78 – 83 (Shore D) |
| HDT@0.45MPa | 200 – 230 (°C) |
| HDT@1.8MPa | 60 – 80 (°C) |
| 난연등급(UL94) | HB |
| Density | 1.2 (g/㎤) |
| Tensile Modulus | 2.8 – 3.3 (GPa) |
| Tensile Strength | 75 – 85 (MPa) |
| Flexural Modulus | 2.8 – 3.5 (GPa) |
| Elongation | 30 – 60 (%) |
| Hardness | 78 – 83 (Shore D) |
| HDT@0.45MPa | 200 – 230 (°C) |
| HDT@1.8MPa | 60 – 80 (°C) |
| 난연등급(UL94) | HB |