A6061 is a Mg-Si alloy. Because of its good corrosion resistance, it is used as a structural material for bolt and rivet joints. It is inferior to the strength of welded joints, but by taking T6 treatment, the reinforcement dimension can be brought to a considerably high value.
| Density | 2.800 (g/㎤) |
| Thermal conductivity | 152~169 (W/(m⋅℃)) |
| Anodizing compatibility | Suitable |
| Magnetism | Non-magnetic |
| Electrical resistivity | 3.9~4.1 (μΩ*㎝) |
| Thermal Expansion Coefficient | 22,7~23,9 X 10^(-6) (C^(-1)) |
| Maximum service temperature | 130~150 (℃) |
| Modulus of elasticity | 68~74 (GPa) |
| Elongation at break | 12~17 (%) |
| Yield strength | 193~290 (MPa) |
| Ultimate tensile strength | 291~320 (MPa) |
| Tensile strength | 300 (MPa) |
| Hardness | 60 (HRB) |
| Density | 2.800 (g/㎤) |
| Thermal conductivity | 152~169 (W/(m⋅℃)) |
| Anodizing compatibility | Suitable |
| Magnetism | Non-magnetic |
| Electrical resistivity | 3.9~4.1 (μΩ*㎝) |
| Thermal Expansion Coefficient | 22,7~23,9 X 10^(-6) (C^(-1)) |
| Maximum service temperature | 130~150 (℃) |
| Modulus of elasticity | 68~74 (GPa) |
| Elongation at break | 12~17 (%) |
| Yield strength | 193~290 (MPa) |
| Ultimate tensile strength | 291~320 (MPa) |
| Tensile strength | 300 (MPa) |
| Hardness | 60 (HRB) |