| Density | 7.900 (g/㎤) |
| Yield strength | 260~483 (MPa) |
| Anodizing compatibility | Not Suitable |
| Magnetism | Magnetic |
| Electrical resistivity | 60 (μΩ*㎝) |
| Thermal conductivity | 26.1~26.3 (W/(m⋅℃)) |
| Thermal Expansion Coefficient | 10.3~12 X 10^(-6) (C^(-1)) |
| Maximum service temperature | 815~870 (℃) |
| Modulus of elasticity | 200 (GPa) |
| Elongation at break | 20~25 (%) |
| Ultimate tensile strength | 450~586 (MPa) |
| Tensile strength | 450 (MPa) |
| Hardness | 85~90 (HRB) |
| Density | 7.900 (g/㎤) |
| Yield strength | 260~483 (MPa) |
| Anodizing compatibility | Not Suitable |
| Magnetism | Magnetic |
| Electrical resistivity | 60 (μΩ*㎝) |
| Thermal conductivity | 26.1~26.3 (W/(m⋅℃)) |
| Thermal Expansion Coefficient | 10.3~12 X 10^(-6) (C^(-1)) |
| Maximum service temperature | 815~870 (℃) |
| Modulus of elasticity | 200 (GPa) |
| Elongation at break | 20~25 (%) |
| Ultimate tensile strength | 450~586 (MPa) |
| Tensile strength | 450 (MPa) |
| Hardness | 85~90 (HRB) |