| Density | 7.900 (g/㎤) |
| Hardness | 75~83 (HRB) |
| Anodizing compatibility | Not Suitable |
| Magnetism | Non-magnetic |
| Electrical resistivity | 65~70 (μΩ*㎝) |
| Thermal conductivity | 29.3~31.7 (W/(m⋅℃)) |
| Thermal Expansion Coefficient | 10.3~12 X 10^(-6) (C^(-1)) |
| Maximum service temperature | 750~925 (℃) |
| Modulus of elasticity | 191~205 (GPa) |
| Elongation at break | 45~60 (%) |
| Yield strength | 190~310 (MPa) |
| Ultimate tensile strength | 480~620 (MPa) |
| Tensile strength | 450 (MPa) |
| Density | 7.900 (g/㎤) |
| Hardness | 75~83 (HRB) |
| Anodizing compatibility | Not Suitable |
| Magnetism | Non-magnetic |
| Electrical resistivity | 65~70 (μΩ*㎝) |
| Thermal conductivity | 29.3~31.7 (W/(m⋅℃)) |
| Thermal Expansion Coefficient | 10.3~12 X 10^(-6) (C^(-1)) |
| Maximum service temperature | 750~925 (℃) |
| Modulus of elasticity | 191~205 (GPa) |
| Elongation at break | 45~60 (%) |
| Yield strength | 190~310 (MPa) |
| Ultimate tensile strength | 480~620 (MPa) |
| Tensile strength | 450 (MPa) |