| Density | 1.200 (g/㎤) |
| Tensile strength | 60 (MPa) |
| Dielectrical Strength | 49 (KV/mm) |
| Thermal conductivity | 0.39 (W(K*m)) |
| Thermal expansion | 13 x 10^(-5) (K^(-1)) |
| HDT | 130 (℃) |
| Glass transition temperature | -60 (℃) |
| Compression strength | 20/35 (MPa) |
| Modulus of elasticity | 2600 (MPa) |
| Impact strength | 8 (KJ/㎡) |
| Elongation at break | 32 (%) |
| Flexural strength | 91 (MPa) |
| Tensile strength | 850 (kg/㎠) |
| Hardness | 85 (shoreD) |