| Density | 1.200 (g/㎤) |
| Hardness | 70 (shoreD) |
| HDT | 70 (℃) |
| Dielectrical Strength | 150 (KV/mm) |
| Surface Resistance | ≥10^(-13) (Xcm) |
| Volume Resistance | ≥10^(-13) (Xcm) |
| Heat Conductivity | 0.25 (W/(K*m)) |
| Thermal Expansion Coefficient | 8.82 X 10^(-6) (C^(-1)) |
| Expansion Coefficient | 10^(-4) (K^(-1)) |
| HDT | 97 (℃) |
| Modulus of elasticity | 2100 (MPa) |
| Modulus of elasticity | 2.2 (GPa) |
| Elongation at break | 2~6 (%) |
| Bending Resistance Strength | 70 (MPa) |
| Yield strength | ≥59 (MPa) |
| Ultimate tensile strength | 33 (MPa) |
| Tensile strength | 62 (MPa) |
| Tensile strength | ≥43 (MPa) |
| Density | 1.200 (g/㎤) |
| Hardness | 70 (shoreD) |
| HDT | 70 (℃) |
| Dielectrical Strength | 150 (KV/mm) |
| Surface Resistance | ≥10^(-13) (Xcm) |
| Volume Resistance | ≥10^(-13) (Xcm) |
| Heat Conductivity | 0.25 (W/(K*m)) |
| Thermal Expansion Coefficient | 8.82 X 10^(-6) (C^(-1)) |
| Expansion Coefficient | 10^(-4) (K^(-1)) |
| HDT | 97 (℃) |
| Modulus of elasticity | 2100 (MPa) |
| Modulus of elasticity | 2.2 (GPa) |
| Elongation at break | 2~6 (%) |
| Bending Resistance Strength | 70 (MPa) |
| Yield strength | ≥59 (MPa) |
| Ultimate tensile strength | 33 (MPa) |
| Tensile strength | 62 (MPa) |
| Tensile strength | ≥43 (MPa) |