| Density | 2.8 (g/㎤) |
| Hardness | 79~86 (HRB) |
| Tensile strength | 524 (MPa) |
| Ultimate tensile strength | 434~580 (MPa) |
| Yield strength | 359~530 (MPa) |
| Elongation at break | 2~11 (%) |
| Modulus of elasticity | 69~76 (GPa) |
| Maximum service temperature | 100 (℃) |
| Thermal Expansion Coefficient | 22.9~24.1 X 10^(-6) (C^(-1)) |
| Thermal conductivity | 131~137 (W/(m⋅℃)) |
| Electrical resistivity | 5.2 (μΩ*㎝) |
| Magnetism | Non-magnetic |
| Anodizing compatibility | Suitable |
| Density | 2.8 (g/㎤) |
| Hardness | 79~86 (HRB) |
| Tensile strength | 524 (MPa) |
| Ultimate tensile strength | 434~580 (MPa) |
| Yield strength | 359~530 (MPa) |
| Elongation at break | 2~11 (%) |
| Modulus of elasticity | 69~76 (GPa) |
| Maximum service temperature | 100 (℃) |
| Thermal Expansion Coefficient | 22.9~24.1 X 10^(-6) (C^(-1)) |
| Thermal conductivity | 131~137 (W/(m⋅℃)) |
| Electrical resistivity | 5.2 (μΩ*㎝) |
| Magnetism | Non-magnetic |
| Anodizing compatibility | Suitable |
| Density | 2.8 (g/㎤) |
| Hardness | 79~86 (HRB) |
| Tensile strength | 524 (MPa) |
| Ultimate tensile strength | 434~580 (MPa) |
| Yield strength | 359~530 (MPa) |
| Elongation at break | 2~11 (%) |
| Modulus of elasticity | 69~76 (GPa) |
| Maximum service temperature | 100 (℃) |
| Thermal Expansion Coefficient | 22.9~24.1 X 10^(-6) (C^(-1)) |
| Thermal conductivity | 131~137 (W/(m⋅℃)) |
| Electrical resistivity | 5.2 (μΩ*㎝) |
| Magnetism | Non-magnetic |
| Anodizing compatibility | Suitable |
| Density | 2.8 (g/㎤) |
| Hardness | 79~86 (HRB) |
| Tensile strength | 524 (MPa) |
| Ultimate tensile strength | 434~580 (MPa) |
| Yield strength | 359~530 (MPa) |
| Elongation at break | 2~11 (%) |
| Modulus of elasticity | 69~76 (GPa) |
| Maximum service temperature | 100 (℃) |
| Thermal Expansion Coefficient | 22.9~24.1 X 10^(-6) (C^(-1)) |
| Thermal conductivity | 131~137 (W/(m⋅℃)) |
| Electrical resistivity | 5.2 (μΩ*㎝) |
| Magnetism | Non-magnetic |
| Anodizing compatibility | Suitable |